L605

Alloy L605 (also referenced as HAYNES® 25) is the strongest of the fabricable cobalt alloys, useful for continuous service to 1800°F. Because of its long and widespread use, this alloy has been the subject of many investigations to determine its properties over a wide range of conditions, thus making it an unusually well characterized material. When exposed for prolonged periods at intermediate temperatures, alloy L605 exhibits a loss of room temperature ductility in much the same fashion as other superalloys, such as alloy X or alloy 625.

L605 is welded using gas tungsten arc, gas metal arc, shielded metal arc, electron beam and resistance welding. Submerged arc welding is not recommended. Use good joint fit-up, minimum restraint, low interpass temperature and cool rapidly from welding. For maximum ductility, fabricated components should be annealed 2150-2250°F, rapid cool.

Inventory

L605 Sheet, L605 Weld Wire

Common Trade Names

HAYNES® 25, L-605 Alloy

Features

  • Outstanding high temperature strength
  • Oxidation resistant to 1800°F
  • Galling resistant
  • Resistant to marine environments, acids and body fluids

Applications

  • Gas turbine engine components such as combustion chambers and afterburners
  • High temperature ball bearings and bearing races
  • Springs
  • Heart valves