Alloy 230 is a nickel-chromium alloy with tungsten and molybdenum additions. It boasts excellent oxidation resistance to 2100°F and superior strength
at temperature. This allows alloy 230 to excel in creep and fatigue resistance at high temperatures. Alloy 230 also exhibits excellent nitriding and
carburization resistance comparable to that of alloy 600. Alloy 230 is welded using 230-W weld fillers designated ERNiCrMo-1.